Abstract
An optimization of a gas metal arc welding (GMAW) process parameter is currently investigated for producing a dissimilar SS400/SUS304 steels joint because a requirement of a sound joint with higher tensile strength. A gas shielding type is one of the important parameter because it could produce a good arc, protect the weld pool from atmosphere and so on. So, this research work aimed to study an effect of the shielding gas type on the mechanical properties of the dissimilar SS400/SUS304 steels butt joint. A relation between microstructure and the mechanical properties of the butt joint was also investigated and compared. The summarized results are as follows. The optimized shielding gas that produced a maximum tensile stregnth of 550 MPa was 95%Ar+5%N2. Nitrogen gas that mixed to the shielding gas affected to decrease dendrite size and to increase the hardness and tensile strength of weld metal. Fracture characteristic of the joint produced by N2 mixed gas showed a larger deformation at the location that was closely the fracture location that implied a ductile behavior. The dissimilar SUS304/SS400 metals joint showed a low hardness base metal, a higher hardness interface and a highest hardness weld metal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.