Abstract
Nanoparticles of Gd3+ ions doped Mn0.5Zn0.5GdxFe2−xO4 (x=0.1, 0.2, 0.3, 0.4) mixed ferrite were prepared using chemical co-precipitation method. The X-ray diffraction measurements confirmed the formation of a cubic spinel structure. The structural parameters like crystallite size, lattice parameter and strain induced have been calculated. The lattice parameter increases with the increase in Gd3+ ion concentration and shows non linear behaviour. HRTEM investigation confirms the nano size formation of the Gd doped Mn–Zn ferrite nanoparticles. EPR was used to evaluate resonance peak intensity, Lande’s splitting factor (g value), peak to peak line width (ΔHp–p), spin concentration (Ns) and relaxation time (τs). Line width, line intensity, relaxation time and spin concentration increase with Gd3+ ions doping (for x=0.1 to x=0.3) and then decrease for x=0.4, whereas the g value shows the reverse trend for the same composition. IR spectra shows two strong absorption bands at 570cm−1 and 416cm−1 of tetrahedral and octahedral bond stretching respectively in all the samples. IR spectrum also shows that Gd3+ occupies the octahedral B-sites. Magnetic parameters such as saturation magnetization (Ms), remanence (Mr) and coercivity (Hc) were measured by search coil method. The value of saturation magnetization increases from 29.94emu/gm for x=0.1 to 46.01emu/gm for x=0.4.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.