Effect of γ (Gamma)-radiation on the physico-mechanical properties of grafted jute fabric reinforced polypropylene (PP) composites

Abstract

The bleached jute fabric (BJF) reinforced polypropylene (PP) composites with various contents of acrylic acid (AA)-treated BJF and un-AA-treated BJF were fabricated by compression moulding method at 190 °C. The AA-grafted BJF reinforced PP composites were then irradiated by γ-ray at various doses. The mechanical properties of neat PP (N-P), ungrafted-BJF and PP composites (UG-BJFPC), AA-grafted-BJF and PP composites (AA-BJFPC) and γ-ray cum AA-grafted-BJF and PP composites (γAA-BJFPC) show maximum tensile strength (TS) of 30, 46, 47 and 51 MPa, maximum flexural strength (FS) of 34, 49, 50 and 54 MPa and maximum Young’s modulus (E) of 280, 428, 436, and 680 MPa, respectively. The increase of TS, FS and E from UG-BJFPC are 2 %, 2 %, and 2 % for AA-BJFPC and 11 %, 10 % and 59 % for γAA-BJFPC. The TS, FS and E are found to increase with radiation dose up to 500Krad and then decrease. The water absorption (WA) for UG-BJFPC, AA-BJFPC and γAA-BJFPC is respectively about 14, 10 and 9 %, indicating a gradual development of hydrophobic character of the composites first by AA-treatment and then by γ-ray-treatment. AA treatment on jute fabric and gamma irradiation on composite result in significant change of morphology of the jute fabric composites surface and better mechanical bonding between fabric and polymer matrix, as a result improved mechanical properties are found.