Abstract
AbstractElectret stability of poly(L‐lactide) (PLA) films, gamma‐irradiated up to 100 kGy has been investigated by measuring the surface potential during the storage period. PLA samples—40‐μm thick films—were prepared by the casting method and then irradiated in a 60Co radiation facility at a dose rate of 0.25 kGy/h. The structural changes during the irradiation were estimated by viscometric, differential scanning calorimetry and scanning electron microscope measurements. Random chain scission and appearance of end radicals are the most probable results of the irradiation process. After irradiation, the samples were charged in a corona discharge system and surface potential was measured by the method of the vibrating electrode with compensation. The values of the surface potential of the irradiated samples were higher in comparison with the non‐irradiated samples. This effect could be related to the degradation of the macromolecules and changes in the crystal state of PLA during the irradiation. Both of the mentioned factors lead to structural defects that increase the number of discrete trapping levels. The effect of low pressure on the surface potential drop was also investigated. © 2012 Wiley Periodicals, Inc. J. Appl. Polym. Sci., 2013
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.