Abstract
ABSTRACTThis paper aims to demonstrate the successful friction stir welding (FSW) conditions of AM20 magnesium alloy. The maximum yield strength and ultimate tensile strength of weld were found to be 75% and 65% of the base metal strength, respectively. The maximum bending angle of the welded joint was 45°. Observations revealed that less plunging depth, high shoulder diameter, and low tool rotational speed and welding speed give better tensile properties. Maximum temperature was observed at 1 mm away from the tool shoulder toward the advancing side. Micro-hardness variation is found to be decreasing along the depth of the weld, and nugget zone (NZ) gives the higher hardness values when compared with base material (BM) and other welded zones. Needle-like grains of the BM became equiaxed grains due to grain recrystalized by the FSW process. The grains in the NZ were finer than thermo-mechanically affected zone and almost same size of grains observed at bottom, middle, and top of the NZ.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.