Abstract
The effect of ion irradiation on the microstructure of oxide dispersion strengthened (ODS) MA956 steel, before and after friction stir welding (FSW), was studied. Both the base material (BM) and welded stir zone (SZ) were irradiated with 5 MeV Fe++ ions at 450 °C up to 25 displacements per atom (dpa). Characterization was performed using scanning transmission electron microscopy (STEM) and atom probe tomography (APT), with particular emphasis on the YAlO dispersoid characteristics and dislocation microstructures. After irradiation, the dispersoids in the BM increased in diameter and decreased in number density, which was explained by an Ostwald ripening mechanism. FSW caused significant coarsening and agglomeration of the dispersoids. After irradiation, both the diameter and number density of the SZ dispersoids increased, which was explained by an irradiation-enhanced diffusion mechanism. Dislocation loop and network behavior was also characterized and large dislocation loops of ≈20 nm diameter formed by 1 dpa in both the BM and SZ samples, whereas the network density remained nearly constant with irradiation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.