Abstract
This letter presents systematic experimental observations of fatigue damage and corresponding dislocation structures in thin Cu films as a function of film thickness made using transmission electron microscopy and focused-ion-beam microscopy. It is found that, in thick films and grains of at least 3.0 μm diameter, coarse surface extrusions and dislocation wall and cell structures occur whereas, in thin films or in small-diameter grains, finer extrusions occur but no clearly defined dislocation structures are present. This minimum required dimension of 3.0 μm for fatigue damage formation may be caused by constrained dislocation motion in small dimensions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.