Abstract
AbstractCommercial stearic acid treated calcium carbonate (CaCO3) was used to make a comparative study on rheological behavior of the CaCO3 and talc‐filled polypropylene (PP) hybrid composites with nontreated filler. Apparent shear viscosity and extrudate swell were investigated with variation of filler ratio and temperature with 30% by weight total of filler was used in PP composite. The Shimadzu capillary rheometer was used to evaluate shear viscosity and shear rate of the composite. It was found that the shear viscosities decrease with increasing shear rate. The apparent shear viscosity of the composite containing the stearic acid treated is slightly lower than untreated filler. Shear thickening behavior at higher shear rate has also shown by 15/15 treated composites at higher temperature about 220°C and investigation by SEM has proved that filler being densely packed at that condition. Treated composites also exhibit lower swelling ratio value than untreated composite, and swelling ratio also decreases linearly with increasing temperature and the die length–diameter ratio. It is believed that dispersion of filler play an important role not only on shear viscosity but also on swelling ratio of PP composite. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 102: 5421–5426, 2006
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.