Abstract
Effect of fiber orientation on tensile and low cycle fatigue of intraply hybrid composites was investigated. In this work, intraply carbon/Kevlar fabric/epoxy hybrid composites were tested for static and cyclic loadings at 0°, 45° and 90° corresponding to carbon, off-axis and Kevlar fiber directions. Ambient fatigue tests were performed at stress levels established from static tests. Tensile results showed the best strength and modulus was in the carbon direction followed by Kevlar direction. At 45°, high ductility was observed associated to fiber rotation. Fatigue linear regression lines indicated a slower degradation rate in the Kevlar loading direction compared to the carbon loading direction. Large fatigue scatter in the Kevlar direction suggested two distinct phases of fatigue attributed to the stiffening of Kevlar fibers that further led to lower fatigue degradation. Investigation on residual strength of run-out samples and fracture modes were also presented with interesting findings.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call