Abstract
Polytetrafluoroethylene (PTFE) matrix has been reinforced by short glass fiber (SGF) with various diameters (8, 4 and 2 μm) in this experiment, and the effects of fiber diameter on the thermal properties of PTFE-based composites, including thermal resistance index (THRI), thermal conductivity (λ), melting temperature (Tm), coefficient of thermal expansion (CTEz) and high-temperature compression-creep, are investigated. The results show that the thermal properties could be improved with the amount of SGF. However, this could be due to the fact that the packings have been compelled by different compression forces caused by composite shrinkage during preparation, the interface between packing with large diameter and PTFE matrix is significantly different from that of the small one, resulting in the crystallinity (Xc), and THRI of PTFE-based composites decreases with the decreasing fiber diameter. Moreover, the small-diameter fiber is easier to debond from PTFE matrix due to the inferior physical stability of interface, the λ decreases with the decrease of the fiber diameter, while CTEz and creep strain value increases. From XRD analysis, the results of crystallite size revealed that the lamella thickness of composite decreases, which means that the Tm of the PTFE-based composites has also decreased with the decreasing fiber diameter.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Materials Science: Materials in Electronics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.