Abstract
Abstract FeTi-FeB was added to molten high chromium white cast iron in amounts of 0.5–2.5 wt% at 50 °C above the melting temperature. The samples were produced in four groups. The first group samples were investigated as cast, the second group homogenized at 1000 °C for 1 h, and the other two groups were also homogenized at 1000 °C but for 3 and 6 h, respectively. To study the effect of FeB and FeTi on the microstructure, the samples were characterized by optical microscopy, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffraction and hardness tests. Wear tests were performed using a pin-on disc. A homogeneously dispersed carbide microstructure was produced by the homogenization heat treatment method. The addition of FeTi-FeB inoculants to high Cr white cast iron played an important role in the distribution of hard carbides. The chemical rate and the carbide volume varied on account of the added hard inoculant particles. TiB2, Cr3C2, M7C3, M23C6, and γ-FeCr phases formed on the surfaces. The hardness and wear resistance were improved considerably due to FeTi-B inoculation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.