Abstract
Iron oxide thin films exhibit structural and magnetic properties that are different from their bulk counterpart. Iron oxide (especially magnetite and maghemite) is one of the most commonly used magnetic materials due to high saturation magnetization M s , and high magnetic susceptibility that makes it a potential candidate for spintronic applications. Iron oxide thin films, with variation in the ratio of Fe 3+ to Fe 2+ cations, are prepared using sol-gel and spin coating method. The ratio of Fe 3+ /Fe 2+ is varied as 1, 1.25, 1.5, 1.75, and 2. For comparative purposes, iron oxide thin films are also prepared using Fe 3+ and Fe 2+ cation, separately. Use of Fe 3+ cations results in the formation of hematite phase of iron oxide along with maghemite while Fe 2+ cations are responsible for the formation of maghemite phase. Varying Fe 3+ /Fe 2+ ratio as 1, 1.25, 1.5, and 1.75 gives maghemite phase, whereas Fe 3+ /Fe 2+ ratio of 2 results in the formation of magnetite phase. Thin films prepared with Fe 2+ cations show ferrimagnetic behavior while a transition to superparamagnetic behavior is observed with variation in Fe 3+ /Fe 2+ ratio as 1, 1.25, 1.50, 1.75, and 2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.