Effect of Fe on the phases and microstructure of TiC–Fe cermets by combustion synthesis/quasi-isostatic pressing

Abstract

Abstract Fully dense TiC–Fe cermets ( x = 10, 20, 30, and 40 wt.%) were produced from Ti–C–Fe powder mixtures by combustion synthesis with quasi-isostatic pressing. The effect of Fe content on combustion temperature, combustion wave velocity, and final product density was investigated. The final product was characterized by XRD, SEM, and TEM. The combustion temperature and wave velocity decreased with increasing Fe content. Product density increased with increasing Fe content (96% at 30 wt.%). X-ray diffraction and transmission electron microscopy (TEM) revealed the final product to contain TiC, Fe phases, lath martensite, and Fe 2 Ti. The TiC particle size decreased with increasing Fe content. In addition, a low density of dislocations was observed in both the TiC particles and Fe binder, indicative of annealing and recrystallization, respectively.