Abstract
Yttria-stabilized zirconia (YSZ) is a potential thermal insulating ceramic for high temperature applications (>1000 °C). YSZ reinforced with multi-walled carbon nanotubes (MWNTs) was processed via spark plasma sintering to produce dense, crack-free homogeneous sample and avoid any degradation of MWNTs when sintered using conventional routes. Despite porosity, the addition of MWNT has a profound effect in improving the damage tolerance of YSZ by allowing the retention of tetragonal phase. However, at some instances, the crack lengths in the MWNT reinforced YSZ matrices have been found to be longer than the standalone counterparts. Therefore, it becomes inappropriate to apply Anstis equation to calculate fracture toughness values. In this regard, a combined analytical cum numerical method is used to estimate the theoretical fracture toughness and quantitatively analyze the mechanics of matrix cracking in the reinforced composite matrices incorporating the effects of various factors (such as far-field stresses, volume fraction of MWNTs, change in the modulus and Poisson's ratio values along with the increase in porosity, and bridging and phase transformation mechanism) affecting the fracture toughness of YSZ-MWNT composites. The results suggest that the incorporation of far-field stresses cannot be ignored in estimating the theoretical fracture toughness of YSZ-MWNT composites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.