Abstract
To evaluate the biaxial flexural strength (BFS), flexural modulus (BFM), and Knoop microhardness (KHN) of incremental and bulk-filled resin-based composites (RBCs) using extended curing exposure times. Disc specimens (n = 8; 6-mm diameter) were fabricated using three stacked molds (0.5-mm thick for the top and bottom molds, and a 1-mm-thick center mold for the conventional and 3-mm thick for the bulk-fill RBCs). Conventional (Tetric EvoCeram/TCE and Filtek Z250/FIZ) and bulk-fill RBCs (Tetric EvoCeram Bulk Fill/TBF and Filtek One Bulk Fill Restorative/FOB) were evaluated. The stacked RBC-filled molds were light-cured for (1) the manufacturer-recommended exposure (MRE) duration; (2) 50%, and (3) 100% extension of the MRE. The BFS, BFM, and KHN of the top and bottom discs were measured. BFS and BFM were analyzed by three-way ANOVA (material*curing time*depth) and Tukey's post hoc (α = 0.05). KHN was analyzed by two-way ANOVA (curing time*depth) and Tukey's post hoc (α = 0.05). Extending the exposure duration did not change the BFS and BFM on the top of the RBCs, but the BFS and KHN increased at the bottom of bulk-fill RBCs. For the conventional RBCs, TCE showed the highest increase on BFS at the bottom, going from 53.6MPa at T1 to 69.9 at T3. Among the bulk-fill RBCs, FOB presented the highest increase on the bottom BFS (T1: 101.0 ± 19.9MPa, T3: 147.6 ± 12.9MPa). For all RBCs and exposure times, BFS and KHN were lower at the bottom. Only FIZ and FOB reached a bottom-to-top hardness ratio of 80%, at T3 and T2. A significant increase on the BFS and KHN on the bottom of bulk-fill RBCs can be observed when the time of exposure to the curing light is double the MRE. However, extended exposure does not eliminate differences on the BFS and KHN between the shallow and deep regions of RBCs. TCE and TBF failed to reach an acceptable B/T hardness ratio at all evaluated exposure times. Mechanical properties of RBCs can be affected by insufficient polymerization, specially at deeper regions of the increment. Therefore, clinicians should consider applying twice the MRE to curing-light to polymerize the maximal increment thickness of bulk-fill RBCs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.