Abstract
AbstractIn order to investigate phase change materials (PCMs) thermal energy storage capacity as well as shape stability, PCM nanocomposites were fabricated by employing modified expanded graphite (EG) as a conductive filler and polyethylene glycol (PEG) PCM. To improve PCM composite shape stability, EG surface has been modified by utilizing Toluene 2 and 4 diisocyanate (TDI), ethylene glycol and PEG 600, respectively. Findings have illustrated that for PEG PCM/modified EG nanocomposites, shape stability was achieved at 5 wt.% of modified EG filler with less than 10% of melt leakage for all prepared samples as a consequence of surface adsorption capacity increment as well as adequate compatibility. Furthermore, phase change efficiency was calculated as 98% and in addition, thermal diffusion at PCM melting temperature range was negligible and approximately equal to zero. To conclude, it could be declared that, fabricated phase change material composite had desirable characteristics along with adequate shape stability for thermal energy storage applications.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.