Abstract
Objective The aim of this study was to assess the combined effect of erbium:yttrium-aluminum-garnet (Er:YAG) laser and mineralizing agents including casein phosphopeptide-amorphous calcium phosphate (CPP-ACP) and fluoride in improving the resistance of demineralized dentin at new demineralization process. Materials and Methods One hundred and twenty healthy dentin surfaces were prepared and demineralized using acidic solutions. Primary microhardness was measured (h1), and samples were randomly divided into six groups. Each group received a different protocol as follows: Group A (control group): no additional treatment, Group B: applying a fluoridated gel, Group C: applying a CPP-ACP-containing cream, Group D: irradiation of Er:YAG laser, Group E: irradiation of Er:YAG laser combined with the application of a fluoridated agent, and Group F: irradiation of Er:YAG laser combined with the application of CPP-ACP-containing cream. Microhardness values were measured afterward (h2). Then, all the groups were re-exposed to acidic solution, and microhardness was measured for the third time (h3). The microhardness data were analyzed using analysis of variance and Scheffe's post hoc test. Results Although application of mineralizing agents increased the microhardness of demineralized dentin in comparison with the control group, no significant difference was observed using two agents. Comparison of laser groups showed an increase in microhardness only after the irradiation of Er:YAG laser combined with the application of a fluoridated agent. Demineralizing process reduced the microhardness values in all the groups, but the application of a CPP-ACP agent caused the least reduction among the laser irradiated groups. Comparison of hardness changes at the beginning and end of the experiment did not show any significant differences between the groups. Conclusion Comparison of treatment modalities used in this study exhibited that fluoride had the greatest impact on dentin resistance. Laser irradiation on demineralized dentin did not increase the hardness or resistance to acidic attacks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.