Abstract
Tests were conducted to determine the fracture toughness of aluminum/FM®73/boron-epoxy adhesively bonded joints. Double cantilever beam (DCB) specimens and end-notched flexure (ENF) specimens were exposed to one of the following environments: hot/wet (71° C(160° F) and >90% RH) conditions for 5000 h, thermal cycles between 71° C (160° F) and −54° C (−65° F), or an outdoor “rooftop” environment for 10 000 h. The environmentally exposed specimens were tested along with as-received (or unexposed specimens). The different adherend materials had different coefficients of thermal expansion (CTE). The mismatch of CTE between adherends caused residual thermal stresses in the adhesive joints at every temperature other than the elevated cure temperature. The residual stresses could not be accounted for with closed form solutions. Finite element analysis (FEA) of the specimens was required. Using FEA solutions, it was determined that the fracture toughness of the environmentally exposed specimens was lower than the as-received specimens for every environment tested for both DCB and ENF specimens.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call