Abstract
The low-temperature performance (LTP) of AB3.42-type La–Y–Ni hydrogen storage alloy was studied by methods of element substitution and surface treatment. The effect of Mn-additive on LTP of La1·3Ce0·5Y4·2Ni19.5-xMnxAl (x = 0, 0.2, 0.5) was systematically investigated. Electrochemical studies showed that Mn-additive deteriorated the LTP of the alloy by reducing platform pressure, deteriorating kinetic performance and forming more oxides on the alloy surface. RE-substitution and hot alkali-ultrasonic treatment of La1.3RE0.5Y4·2Ni19·5Al (RE = Ce, Sm, Nd) alloys were applied to further optimize the LTP. The maximum discharge capacity and capacity retention at the 100th cycle of La1·3Ce0·5Y4·2Ni19·5Al alloy were 252.1 mA h/g and 87.1% at 243 K, respectively. Furthermore, the LTP of RE-substitution alloys at 243 K was conspicuously improved by surface treatment, which were raised from 214.7 mA h/g to 301.1 mA h/g by Sm-substitute, from 220.9 mA h/g to 303.9 mA h/g by Nd-substitute and from 252.1 mA h/g to 254.8 mA h/g by Ce-substitute.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.