Abstract
Ethylene-vinyl acetate copolymer (EVA) flame retarded by a combination of intumescent flame retardants (IFR) and organically modified montmorillonite (OMMT) have been crosslinked by high-energy electron beam irradiation. The structure was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The effects of electron beam irradiation on the thermal, mechanical and dynamic mechanical properties of the irradiated EVA nanocomposites were investigated. The XRD and TEM results demonstrated that the OMMT was well dispersed in the EVA nanocomposites. The LOI and UL-94 results showed that a synergistic effect on the flame retardancy of EVA nanocomposite existed between the IFR and OMMT. With the addition of 1 wt% OMMT and 24 wt% IFR, the LOI value of EVA/IFR/OMMT nanocomposite increased from 30.5 % to 33.5 %. The mechanical properties of the irradiated EVA nanocomposite were evidently improved at 160 kGy dosage with the increase in the tensile strength to 18.5 MPa. Thermal oxidative degradation of the flame-retardant EVA/IFR/OMMT nanocomposites was characterized by thermogravimetric analysis/infrared spectrometry (TG–IR) and real-time Fourier transformed infrared spectroscopy (RT-FTIR).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.