Abstract
In this study, we successfully prepared the pure PVDF film containing almost exclusive γ-phase (γ-PVDF) using 15wt% solution in N, N-dimethylformamide. These γ-PVDF films were irradiated by 3.0MeV electron beam in vacuum at room temperature up to 358 kGy. The effect of the irradiation on the chemical structural and thermal properties of pristine and irradiated γ-PVDF films were detailedly investigated by FTIR, XRD and DSC, respectively. DSC results show that two single and different melting endotherms from the successive heating curves correspond to γ-phase and α-phase, respectively. FTIR results show that the characteristic absorption peaks corresponding to γ-phase do not shift, and the C˭C bond formation is not significantly observed in the irradiated γ-PVDF films until above 30 kGy. XRD results show that the crystal form of γ-PVDF is not influenced significantly by irradiation. All PVDF films exhibit a single melting endotherm, irrespective of the irradiation dose. Two superpositioned crystallization peaks were observed for PVDF films only irradiated at high dose of 232 and 358 kGy, which can be related to the fractionated crystallization of irradiated PVDF. The dependences of thermal characteristics on the irradiation dose were detailedly investigated by DSC in this study.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.