Effect of Electrolyte Concentration on Anodised Titanium in Mixture of β-Glycerophosphate (β-GP) and Calcium Acetate (CA)

Abstract

Anodic oxidation is a surface modification method which combines electric field driven metal and oxygen ion diffusion for formation of oxide layer on the anode surface. Anodised titanium has been widely use in biomedical applications especially in dental implant. This study aimed to investigate the effect of electrolyte concentration on titanium. Specifically, the titanium foil was anodised in mixture of β-glycerophosphate disodium salt pentahydrate (β-GP) and calcium acetate monohydrate (CA) with different concentration (0.02 M + 0.2 M and 0.04 M + 0.4 M), anodising time (10 min), applied voltage (150, 200, 250, 300 and 350 V) and current density (10 mA.cm-2) at room temperature. Surface oxide properties of anodised titanium were characterised by using glancing angle X-ray diffraction (GAXRD), field emission scanning electron microscope (FESEM), focused ion beam (FIB) milling and digital camera. With increasing electrolyte concentration, the oxide layer became more porous. The GAXRD results also showed that rutile formed at high applied voltage (≥300 V) when the higher concentration of electrolyte was used.