Abstract
The sintered Nd14.1Co1.34Cu0.04FebalB5.84 permanent magnets with DyHx addition have been prepared by powder-blending technique. The magnetic properties and microstructures of the magnets were investigated. It was found that Dy element is enriched in the intergranular phase, being evenly distributed throughout the grain boundary and improving the orientation of magnets as a lubricant, and 1.2% to 2% DyHx additions are proved to be very effective in improving the permanent magnetic properties of Nd14.1Co1.34Cu0.04FebalB5.84 magnets. Further analysis revealed that the increase of coercivity and slight decrease of remanence due to DyHx addition can be attributed to the reduction of the primary phase volume, formation of the (NdDy)-rich phase and grain refinement of the main phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.