Abstract

The effect of dissolved hydrogen (DH) on primary water stress corrosion cracking of nickel base alloys has been of intense interest for plant operators worldwide. In this study, crack growth rates of Alloy 600 were measured in simulated PWR primary coolant at 330 °C with DH levels of 5, 16, 45 and 75 cc H2/kg H2O, respectively. The oxide films formed in the crack tip regions were examined using transmission electron microscopy (TEM). The results show low and similar crack growth rates at all DH levels, without a maximum at 16 cc H2/kg H2O. The low DH content favors nickel oxide formation at the crack tip region, whereas the high DH level favors Me3O4 type spinel formation. Also, the oxide films were found to grow epitaxially on some metal grain surfaces in the cracks. The possible effects of alloy composition on the oxide films formed, and the effect of DH on the crack growth are briefly discussed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.