Abstract
The influence of some parameters controlling the hydroxyapatite (HA) suspension rheology in terms of heat treatment of the HA powder prior to suspension preparation, suspension solid loading and the amount of corn starch addition was thoroughly investigated. The heat treatment of powder at 1100?C prior to suspension preparation was found to be extremely efficient in preparing suspensions with high solid loading of 59 vol.%. In contrast, the highest solid loading that could be developed from the non-heat treated powder was 14 vol.%. This phenomenon is consequence of the changes in the physical and chemical properties of the powder after the heat treatment step. The amount of native corn starch addition has ranged from 10 to 40 vol.%. The addition of corn starch leads to the high retardation in the suspension viscosity, particularly at low shear rate. On the contrary, at higher shear rate the situation is completely different. The properties of the consolidated green sample (produced from suspensions containing various corn starch amounts) in terms of relative density and compressive strength were studied. The results indicated that even though there were no considerable changes in the relative density, the compressive strength was sharply increased with increasing starch amount content until it reached a maximum at 30 vol.% and then decreased thereafter.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.