Abstract
In this research, cordierite was produced using oxide based raw materials (MgO, SiO2 and Al2O3) through glass route method. A mixture of raw material was gone through melting at 1550 °C followed by water quenching. Glass powder produced were then milled for 5 hour to get fine powder. Cordierite powder produced was then used to prepare 3-D porous cordierite ceramic. In this research, gelcasting method was choosen. The dispersant amount added in the cordierite slurry was varied (2.5-5.5g). The cordierite pellet were then characterized using x-ray difraction. Results shows high purity (99%) cordierite was obtained. The porosity and compressive strength were tested. The porosity show when increasing the dispersant amount, the porosity will decrease. For compressive strength increase when the dispersant amount increase.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.