Effect of dislocations on the growth of p-type GaN and on the characteristics of p-n diodes

Abstract

We investigate the influence of crystal defects on p-type GaN grown by metalorganic vapor phase epitaxy. Sets of p-type GaN films were grown on sapphire substrates and on free-standing GaN (F-GaN) substrates simultaneously using various Et-Cp2Mg flow rates. Although there is a difference of two orders of magnitude between the threading dislocation densities of p-type GaN grown on sapphire and F-GaN substrates, there is no significant difference in hole concentration. However, there are problems with the surface morphology of p-type GaN grown on sapphire. The deterioration of the surface was caused by the difference in nanopipe density. The electrical properties of a p–n junction diode formed on sapphire with a high density of nanopipes were observed using emission microscopy under both forward- and reverse-bias conditions. Our results demonstrate that the nanopipes are electrically inactive, and that other types of threading dislocation have more influence on the current–voltage characteristics.