Abstract
BackgroundSeveral interfacial surface treatments of zirconia surfaces have been proposed to improve adhesion to ceramic veneering. However, information regarding the durability and effect of such treatments on the bond strength following such treatments is lacking.Aim of the studyThis study aimed to evaluate the shear bond strength between veneering ceramic and zirconia core after different interfacial surface treatments.Materials and methodsFifty-two discs (8 mm in diameter and 3 mm in height) were fabricated from zirconia blanks using a microtome cutting machine. Zirconia discs were divided into four groups (n = 13). Group I was subjected to air-borne abrasion using (Al2O3), group II was coated by bioglass, group III was coated with ZirLiner, and group IV was subjected to wash firing (sprinkle technique). A cylinder (4 mm in diameter and 3 mm in height) of veneering ceramic was fired on top of the zirconia core. Shear bond strength (SBS) between zirconia core and veneering ceramic was evaluated by using a universal testing machine. The data was collected and statistically analysed using One-Way ANOVA followed by multiple pairwise comparisons using Bonferroni adjusted significance level. The failure modes were assessed using a stereomicroscope for each group.ResultsThe highest mean bond strength was recorded in group III (17.98 ± 2.51 MPa), followed by group II (15.10 ± 4.53 MPa), then group I 14.65 ± 2.97 MPa. The lowest mean bond strength was recorded in group IV (13.28 ± 3.55 MPa).ConclusionsSurface treatments had an effect on the zirconia-veneer shear bond strength. Liner coating revealed the highest shear bond strength values, significantly higher in comparison to wash firing (sprinkle technique) .
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.