Abstract
PurposeThe objective of the study was to investigate the effect of different immersion times, in coloring liquid, and sintering temperatures on translucency of monolithic nanocrystalline zirconia. Materials and methodsForty five specimens of nanocrystalline zirconia were obtained by cutting InCoris TZI blocks into slices using a stainless steel disc mounted on a custom made milling machine. The slices were divide into three groups (n = 15) according to immersion times (3,5 and 7 min) then each group was further subdivided into 3 subgroups (n = 5) according to the sintering temperatures (1400°c, 1500°c and 1600°c). CIE-Lab coordinates were measured for each slice against black and white backgrounds using Vita easy shade spectrophotometer and translucency parameter (TP) was calculated. One way analysis of variance combined with a Tukey-post hoc test were used to analyze the data obtained (P = 0.05). ResultsResults of the present study showed that at temperature 1400°c there was statistically significant decrease in TP between 7 min immersion time and the other two groups, while there was no statistically significant difference in TP using different immersion times at temperatures 1500°c and 1600°c. ConclusionOur results showed that the best translucency was obtained by the combination between lower dipping times and higher sintering holding temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.