Abstract
The article presents the results of an analysis of the surface roughness parameters, microhardness, and the stresses of the surface layer ofFSW butt joints subjected to the burnishing process with a diamond tip. This can be useful in selecting the optimal parameters of the burnishing process, ensuring the best properties of the surface layer of the FSW joint. Burnishing force and feed rate influence were analyzed according to the two-factor three-level full factorial statistical completed plan PS/DC 32. The tested material was 2024-T3 aluminum alloy sheets with a thickness of 2 mm. The results show that burnishing significantly reduced the surface roughness from Sa = 6.46 μm to Sa in the range of 0.33 μm–1.7 μm. This treatment provides high compressive residual stresses σx from −86 to −130 MPa and σy from −158 to −242 MPa. Microhardness increased from 84.19% to 174.53% compared to butt joints. Based on the obtained results, multi-criteria optimization was carried out. This optimization allows us to obtain a compromise solution ensuring compressive stresses in the surface layer (σx=−123 MPa and σy=−202 MPa) and microhardness HV=362.56 mm/mm2 with the roughness of the weld surface Sa = 0.28 µm, Sku = 3.93 and Spc = 35.88 1/mm.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.