Abstract
Objective:The objective of this study was to assess the effect of dental acid etchant (DAE)-mediated photodynamic therapy on bacterial reduction and microshear bond strength of composite to dentin.Materials and Methods:Eighty permanent third molars after sample preparation were exposed to a cariogenic challenge with Streptococcus mutans. After incubation, specimens were randomly divided into four groups (n = 20): Group I – DAE, Group II – low-level laser (LLL), Group III – diode laser + methylene blue (MB + L), and Group IV – diode laser + DAE (DAE + L). Half of the specimens from each group were selected for bacterial reduction assessment and the other half for microshear bond strength. All the samples for assessment of bacterial reduction (before and after intervention) were seeded onto the surface of mitis-salivarius-bacitracin medium. After incubation, the viable bacterial count was determined in colony-forming unit/mL. For microshear bond strength assessment, samples were subjected to various treatment modalities and then bonding and debonding procedure was performed for blocks of composite and values were recorded.Results:Significant reductions in S. mutans were observed in all the groups – Group I (DAE) 68.50%, Group II (LLL) 55.90%, Group III (MB + L) 88.60%, and Group IV (DAE + L) 87% with comparable bacterial reduction between Group III (MB + L) and Group IV (DAE + L). Furthermore, a significant difference in bond strength values was seen in Group III (MB + L) 10.99 MPa and Group IV (DAE + L) 17.99 MPa whereas an insignificant difference was found between Group I (DAE) 20.74 MPa, Group II (LLL) 18.27 MPa, and Group IV (DAE + L).Conclusion:DAE caused a comparable reduction in bacterial count to MB-assisted PDT and also there was no adverse effect on bond strength values. PDT can be performed while acid etchant containing MB dye is being applied in the cavity, thus reducing operative time and enhancing cavity disinfection.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.