Abstract
Extensive research on the effect of spark-plasma sintering and free forging on the microstructure, transformation temperature, and superelasticity of Ti-23at% Nb shape-memory alloys (SMAs) was undertaken. Based on the obtained results, it was found that the specimen showed significant results after deformation than the homogenization step, from which it can be concluded that the deformation has considerable effects on the mechanical properties and shape-memory characteristics of Ti-based SMAs. The microstructure of homogenized and deformed Ti-23at% Nb SMAs consists of β, α, α′ and ω phases, while the sintered sample shows only β and α phases. Endothermic and exothermic peaks of the austenite↔martensite transformation are seen in the homogenized sample, then after being deformed, the exothermic peak disappeared. The highest austenite start and finish temperatures were observed with the deformed sample due to disappearance of TiNb4 intermetallic compounds and a high percentage of β phase. The ductility of the deformed sample shows the highest value compared with the homogenized sample due the elimination of coarse α precipitates and brittle intermetallic compounds of TiNb4, along with the suppression of the brittle ω phase and retaining β matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.