Abstract
Evaluation of creep–fatigue failure is essential in design and fitness evaluation of high-temperature components in power generation plants. Cyclic deformation may alter the creep properties of the material and taking cyclic effects into account may improve the accuracy of creep–fatigue failure life prediction. To evaluate such a possibility, creep tests were conducted on 316FR and modified 9Cr–1Mo steel specimens subjected to prior cyclic loading; their creep deformation and rupture behaviours were compared with those of as-received materials. It was found that creep rupture life and elongation generally decreased following cyclic loading in both materials. In particular, the rupture elongation of 316FR in long-term creep conditions drastically decreases as a result of being cyclically deformed at a large strain range. Use of creep rupture properties after cyclic deformation, instead of those of as-received material, in strain-based and energy-based life estimation approaches brought about a clear improvement of creep–fatigue life prediction.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.