Abstract
X65 low carbon steel was exposed to Co-60 radiation source with 1.25MeV gamma rays, and cumulatively absorbed gamma irradiation doses (1, 2, and 3MGy) were obtained after different exposure time (333, 667, and 1000h). The effect of cumulative gamma irradiation on microstructure and corrosion behaviour of the carbon steel in unirradiated aerobic Beishan groundwater at 25°C was investigated by using positron annihilation, scanning vibrating electrode, and electrochemical techniques. Cumulative gamma irradiation increases vacancy intensity and decreases open circuit potential (OCP) of carbon steel. They indicate that the irradiated carbon steel is activated. Measured current density distribution above the irradiated carbon steel shows that cumulative gamma irradiation accelerates localized corrosion after 0.5h of immersion. In contrast, the analysis of electrochemical impedance spectroscopy of the irradiated carbon steel indicates that localized corrosion is transformed into general corrosion after 12h of immersion, which is also accelerated by cumulative gamma irradiation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call