Abstract
In this paper, detailed properties of Ti-Al-Si-N nanocomposite films doped with Cu additive at various concentrations are studied and followed with careful discussion. Deposited on high speed steel substrates with the assistance of vacuum cathode arc ion plating, the film composition and crystallinity can be controlled by changing the target composition. Then the film structure, chemical and phase composition, mechanical and tribological properties are characterized by X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), field emission scanning electron microscope (FESEM) and high resolution transmission electron microscopy (HRTEM), atomic force microscopy (AFM), nanoindentation and Rockwell indenter. The results indicate that with increasing copper content in the film systems, a reduction of the grain size and a deterioration of the preferred orientation were detected by XRD and HRTEM. Furthermore the film hardness H and the elastic modulus E decrease from 35±6 to 13±1GPa and from 286±26 to 163±13GPa, respectively. The ratio H3/E2 is calculated on basis of measurements of hardness H and Young's modulus E. The adhesive strength between the film and the substrate is strongly improved, compared to others without Cu additive, as well as the tribological performance of the films. This whole study implies that these Cu-doped nanocomposite films deserve some cautiousness before its application for wear resistance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.