Abstract
Fe2Mn1-xCrxSi (x = 0, 0.1, and 0.2) alloys were investigated for their magnetic and transport properties in view of the expected half metallicity. It is found that Cr substitution suppresses the antiferromagnetic phase present in parent Fe2MnSi, which completely disappears for x = 0.2. Curie temperature of the alloys increases from 230 K to 299 K as x is increased from 0 to 0.2. The value of the Rhodes-Wohlfarth ratio indicates that the system shows iterant magnetism. Resistivity measurements also show absence of antiferromagnetic phase for x = 0.2. Resistivity data have been fitted by considering the electron-phonon and electron-magnon scattering contributions, which indicates the presence of half metallicity in these compounds. Temperature dependence of resistivity data shows magnetoresistance of −3% and −2.5% at Curie temperature with applied field of 50 kOe for x = 0.1 and 0.2, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.