Abstract
Hydrogen (H) behaviour in materials was investigated in rapidly solidified (RS) foils of pure aluminium (Al), Al-0.4 Cr and Al-0.25 Zr alloys (at %) by means of thermal desorption spectroscopy (TDS). In addition, Al-0.25; 0.3 Zr alloys were examined with respect to microstructure and its instability during the thermal process using SEM and microhardness measurements. The effect of dopes and heating rate on H desorption was summarized. The lowest energy desorption is attributed with significant thermal desorption peak which temperature was found is correlated with sample composition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.