Abstract
In the present paper, the effect of counter surface temperature and load on the transition from mild to severe wear of A319/15%SiCp, A336/15%SiCp, and A390/15%SiCp composites have been reported. Composites were produced through stir casting route. Adhesive wear behavior of composites was studied under dry reciprocating conditions using indigenously developed reciprocating friction wear test rig conforming to ASTM standard G133-05. It was found that increase in counter surface temperature increases wear rate and depending upon the load and type of composite mode of wear changes from mild oxidative to severe metallic wear noticed. At 120N load, the critical transition temperature for all the three Al-Si-SiCp composites was found to be 350°C. SEM study of wear surface and wear debris was conducted to analyze the mode of wear and operating wear mechanism. Severe wear was characterized by massive plastic deformation and gross material removal while the mild wear was found to be associated with delamination and scoring as main wear mechanisms responsible for material loss.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.