Abstract
We describe here the effect of cooling rate on the microstructure and mechanical properties of Nb-microalloyed steels that were processed as structural beams at three different cooling rates. Nb-microalloyed steels exhibited increase in yield strength with increase in cooling rate during processing. However, the increase in the yield strength was not accompanied by loss in toughness. The microstructure at conventional cooling rate, primarily consisted of polygonal ferrite-pearlite microconstituents, while at intermediate cooling rate besides polygonal ferrite and pearlite contained significant fraction of degenerated pearlite and lath-type ferrite. At higher cooling rate, predominantly, lath-type (acicular) or bainitic ferrite was obtained. The precipitation characteristics were similar at the three cooling rates investigated with precipitation occurring at grain boundaries, on dislocations, and in the ferrite matrix. The fine scale (∼8–12 nm) precipitates in the ferrite matrix were MC type of niobium carbides. The microstructural studies suggest that the increase in toughness of Nb-microalloyed steels with increase in cooling rate is related to the change in the microstructure from predominantly ferrite-pearlite to predominantly bainitic ferrite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.