Abstract
Cu 3 Sn is indeed the e phase in the Copper-Tin system, which is one of the main phase of High Copper Amalgam Alloy (Ag-Sn-Cu Alloy) and at present very little emphasis has been placed on the microstructure and the mechanical properties of Cu 3 Sn phase. In this study 3 castings of Cu-38.37 wt% Sn were produced. The casting specimens were subjected to different cooling rate conditions: as cast, air blown, and water quenched. The possible phases were identified by x-ray diffraction and the microstructure were examined on a metallurgy optical microscope. An ultrasonic equipment were utilized for longitudinal wave velocity measurements. Using this velocity the longitudinal modulus can be calculated. Phase identification on as cast, air blown and water quenched specimens indicated that the specimens consist of e (Cu 3 Sn) phase. The smaller and finer microstructure of Cu 3 Sn phase was produced from water quenched (faster cooling rate) specimen. However its longitudinal modulus is significantly lower than the longitudinal modulus of as cast and air blown specimens. Therefore it is still need further investigation in order to obtain the transversal wave velocity and the Young's modulus.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.