Abstract
Precipitated phase of microalloyed H beam was analysed by TEM and electrolyzation. Effect of heating temperature on austenite grain size and solid solution of Nb in steel and effect of finishing rolling temperature on property of tested steel were studied. According to the results, controlled rolling process was determined to produce the hot-rolled. Property of H beam includes that yield strength is 410MPa~430MPa, and charpy impact energy at -20°C is greater than 50J. The ferrite grain size number is 11. All of the properties are up to the American Petroleum Institute standard of H beam for offshore platforms.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.