Abstract
AbstractSyntactic foams are strong, lightweight materials that can be useful in marine and aeronautical applications. However, these materials are brittle, which can limit their usefulness. The fracture toughness of several epoxy based syntactic foams, as affected by foam composition, was evaluated. The parameters of interest were the curing agent type (anhydride and amine) and elastomer type and level. For the anhydride curing agents studied, the addition of elastomer improved the fracture toughness, and no reduction in flexural strength was observed upon elastomer addition. Examination of the fracture surface showed that the failure mechanism varied with foam composition, from crack propagation around the microballoon filler to crack propagation through the filler, possibly explaining the strength results. For a syntactic foam cured with a cycloaliphatic amine curing agent, the addition of elastomer did not significantly affect the fracture toughness. Examination of the fracture surface showed that the failure mechanism for the syntactic foam compositions with and without added elastomer was crack propagation through the matrix rather than through the microballoon filler. Polym. Compos. 25:229–236, 2004. © 2004 Society of Plastics Engineers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.