Effect of Combined Application of Hydrofluoric and Phosphoric Acids and Active Irrigation with a Microbrush on Shear Bond Strength of Lithium Disilicate Ceramics to Enamel.

Abstract

This study assessed the effect of combined application of hydrofluoric (HF) acid and phosphoric acid (PA) and active irrigation (AI) with a microbrush on shear bond strength (SBS) of lithium disilicate (LDS) ceramics to enamel. This in vitro study was conducted on 40 extracted teeth that received enamel preparation with a #12 cylindrical bur. Forty IPS e.max LT rods (3mm diameter, 6mm height) were fabricated and randomly assigned to four groups (n = 10) for surface treatment with 5% HF (group 1), 5% HF and AI with a microbrush for 20 seconds (group 2), 5% HF and 32% PA (group 3), and 5% HF and 32% PA plus AI with a microbrush for 20 seconds (group 4). Silane and Choice 2 cement were used for bonding rods to enamel. The SBS was measured by a universal testing machine. Data were analyzed by two-way analysis of variance (ANOVA), Bonferroni, and Chi-square tests (alpha = 0.05). Group 4 had the highest SBS, and group 1 had the lowest SBS (P < 0.05). Group 2 had a significantly higher SBS than group 1, and group 4 had a significantly higher SBS than group 3. AI with a microbrush significantly increased the SBS (P < 0.05), but the application of PA caused no significant change in SBS (P > 0.05). The interaction effect of PA and AI on SBS was not significant (P > 0.05). The application of PA in addition to 5% HF acid caused no significant change in the SBS of LDS ceramic to enamel. However, AI with a microbrush significantly increased the SBS.