Abstract
The coarsening behaviors of γ″-phase particles in Inconel 718 alloy aged at 750, 800, and 850°C were investigated by scanning electron microscopy (SEM). Detailed observations and quantitative measurements were conducted to characterize the coarsening behavior of the γ?-phase under various aging conditions. The experimental results indicate that the existence of the δ-phase retards the formation and coarsening of the γ″-phase, without influencing its final particle size or amount. Moreover, when cold rolled with a reduction of 50%, the dimensions of the γ″ particles in Inconel 718 alloy decrease with increasing aging time. Furthermore, the coarsening behavior of the γ″-phase in the Inconel 718 alloy after a normal aging treatment (sample A) and that of the primary δ-phase (sample B) follow the Lifshitz–Slyozov–Wagner (LSW) diffusion-controlled growth theory; the thus-obtained activation energies for the γ″-phase are 292 kJ·mol-1 and 302 kJ·mol-1, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.