Abstract
Hot pressing sintering process for cemented carbide preparation was investigated with cBN-WC/Co composite powders with different Co content from 4wt% to 10wt% at temperatures between 1300°C and 1400°C. The results showed that the Co content had remarkable influence on the densification and mechanical properties of cBN-WC/Co composites. Near-full densification can be obtained when cBN-WC/8wt%Co powders were sintered at temperatures at 1350°C, and pressures at 20MPa, combining an excellent Vickers hardness of 17.57GPa with an acceptable flexure strength of 601.58MPa.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.