Abstract
Series of TiCN-TiB2 cermets were in situ prepared from the TiCN-B4C-Ti-Co system via spark plasma sintering (SPS). The effects of Co content on the densification, microstructure, mechanical properties, and wear resistance of TiCN-TiB2 cermets were investigated. The results showed that the Co addition had little effect on the phase composition of the sintered cermets, but had significant influences on the densification, microstructure and mechanical properties. Appropriate addition of metal Co could enhance densification and promote the grain growth of ceramic phases, but excessive addition resulted in a decrease in hardness and wear resistance. When the Co content was 10 wt.%, the cermet obtained the optimal comprehensive performance (a hardness of 1757 HV and a fracture toughness of 7.02 MPa•m1/2). Meanwhile, the cermets with 10 wt.% Co addition exhibited optimum wear resistance properties due to a good combination of hardness and toughness and moderate grain size. In addition, the formation process and strengthening mechanism in present system were discussed in detail. Results from this work could provide valuable references for the fabrication of TiB2 reinforced TiCN-based cermets.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.