Abstract
Ni-Co coatings with various cobalt contents were electrodeposited from modified Watts bath. The effect of cobalt content on electrodeposition mechanism of the coatings was studied by electro-chemical impedance spectroscopy method (EIS). Surface morphology and crystallographic structure of the coatings were investigated by means of SEM and XRD. Mechanical properties of the coatings were determined using Vickers microhardness and tensile tests. It was found that with increasing the Co2+ ions in electroplating bath, the charge transfer resistance (Rct) of Ni–Co film increased whereas the Warburg impedence decreased. This may be due to enhancement in coverage of cathode surface by Co(OH)2 and higher diffusion rate of metal ions towards cathode surface, respectively. Also, with increasing the cobalt content in the bath, cobalt content in the alloy coating increased anomalously and (111) texture consolidated gradually. With increasing the cobalt content up to 45% in alloy coating, the grain size decreased and consequently, hardness and strength of the alloy increased. Further enhancement of cobalt content up to 55% led to a little decrease in hardness and strength. The maximum ductility was observed for Ni–25%Co coating due to relatively small grain size and compact structure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.