Abstract
The effects of substituting chromium for iron and the use of low cost ferrochromium alloys in the production of β-Ti–Fe–Cr alloys have been studied with respect to phase constitution, stability, and mechanical properties, in solution treated and quenched states using resistivity, hardness measurement, X-ray diffraction, and tensile testing. Resistivity at room and liquid nitrogen temperatures, and hardness decreased while the ratio of resistivity at liquid nitrogen temperature to that at room temperature increased with increases in chromium content. Alloys of Ti–Fe–Cr, with almost the same electron per atom value, with higher chromium content have smaller volume fractions of athermal omega than alloys with higher iron content. There is less solution hardening in the former alloys than in the latter alloys. Tensile strength decreased with increases in chromium content, while elongation and reduction in area significantly increased. The balance between tensile strength and ductility (elongation and reduction in area) improved in the alloys with added chromium as a substitute for iron. Therefore, no negative influences of ferrochromium alloying on mechanical properties was observed in this study.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.