Abstract
The effects of chromium and silicon modification on the microstructure and hot corrosion resistance of slurry aluminide coatings applied on pure nickel was studied by in-depth microscopic analyses. The simple and the Cr-modified aluminide coatings provided limited protection in Type II hot corrosion conditions but the Si-modified coating exhibited outstanding resistance with no sign of attack after 300 h of isothermal exposure at 700 °C. The synergistic dissolution between NiO and Al2O3/Cr2O3 appears responsible for the onset of the corrosion attack for the simple and Cr-modified coatings while silicon is shown to extend the incubation period.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.