Abstract
Polycaprolactone nanofibers were prepared using five different solvents (glacial acetic acid, 90% acetic acid, methylene chloride/DMF 4/1, glacial formic acid, and formic acid/acetone 4/1) by electrospinning process. The effect of solution concentrations (5%, 10%, 15% and 20%) and applied voltages during spinning (10 KV to 20 KV) on the nanofibers formation, morphology, and structure were investigated. SEM micrographs showed successful production of PCL nanofibers with different solvents. With increasing the polymer concentration, the average diameter of nanofibers increases. In glacial acetic acid solvent, above 15% concentration bimodal web without beads was obtained. In MC/DMF beads was observed only at 5% solution concentration. However, in glacial formic acid a uniform web without beads were obtained above 10% and the nanofibers were brittle. In formic acid/acetone solution the PCL web formed showed lots of beads along with fine fibers. Increasing applied voltage resulted in fibers with larger diameter.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.